Description:
ASTM A517 Steel Plates: A517 grade A, A517 grade B, A517 grade E, A517 grade F, A517 grade H, A517 grade P, A517 grade Q, A517 grade S
ASTM A517 steel plates are high-strength quenched and tempered alloy steel plates intended for use in fusion welded boilers and other pressure vessels.
The maximum thickness of A517 alloy steel plates shall be as follows:
A517 Gr A, A517 Gr B steel plate thickness ≤1.25 in. [32 mm]
A517 Gr H, A517 Gr S steel plate thickness ≤2 in. [50 mm]
A517 Gr P steel plate thickness ≤4 in. [100 mm]
A517 Gr F steel plate thickness ≤2.50 in. [65 mm]
A517 Gr E, A517 Gr Q steel plate thickness ≤6 in. [150 mm]
ASTM A517 Steel Plate Chemical Composition: | ||||||||
Thk | ≤32mm | ≤32mm | ≤150mm | ≤65mm | ≤50mm | ≤100mm | ≤150mm | ≤50mm |
A517 | A517GrA | A517GrB | A517GrE | A517GrF | A517GrH | A517GrP | A517GrQ | A517GrS |
C | 0.13-0.23 | 0.13-0.23 | 0.10-0.22 | 0.08-0.22 | 0.10-0.23 | 0.10-0.23 | 0.12-0.23 | 0.10-0.22 |
Mn | 0.74-1.20 | 0.64-1.10 | 0.35-0.78 | 0.55-1.10 | 0.87-1.41 | 0.40-0.78 | 0.87-1.41 | 1.02-1.62 |
Si | 0.34-0.86 | 0.13-0.37 | 0.08-0.45 | 0.13-0.37 | 0.13-0.37 | 0.18-0.37 | 0.13-0.37 | 0.13-0.45 |
Ni | … | … | … | 0.67-1.03 | 0.27-0.73 | 1.15-1.55 | 1.15-1.55 | |
Cr | 0.46-0.84 | 0.36-0.69 | 1.34-2.06 | 0.36-0.69 | 0.36-0.69 | 0.79-1.26 | 0.94-1.56 | |
Mo | 0.15-0.31 | 0.12-0.28 | 0.36-0.64 | 0.36-0.64 | 0.17-0.33 | 0.41-0.64 | 0.36-0.64 | 0.10-0.38 |
V | … | 0.02-0.09 | … | 0.02-0.09 | 0.02-0.09 | … | 0.02-0.09 | |
Ti | … | 0.01-0.05 | 0.005-0.11 | 0.11 max | 0.11 max | 0.11 max | 0.07 max | |
Zr | 0.04-0.16 | … | … | … | … | |||
Cu | … | … | … | 0.12-0.53 | … | |||
Nb | … | … | … | … | … | 0.07 |
ASTM A517 Steel Plate Mechanical Properties: | |||
ASTM A517 | Tensile strength | Yield strength | Elongation in |
Thickness | ksi [Mpa] | ksi [Mpa] min. | 2in. [50mm] |
2.5in. [65mm] and under | 115-135 [795-930] | 100 [690] | ≥16% |
2.5-6in. [65mm-150mm] | 105-135 [725-930] | 90 [620] | ≥14% |
Standard | Boiler and Pressure Vessel Steel Grades | |||
ASTM A202/A202M | A202 Grade A | A202 Grade B | ||
ASTM A203/A203M | A203 Grade A | A203 Grade B | A203 Grade D | A203 Grade E |
A203 Grade F | ||||
ASTM A204/A204M | A204 Grade A | A204 Grade B | A204 Grade C | |
ASTM A285/A285M | A285 Grade A | A285 Grade B | A285 Grade C | |
ASTM A299/A299M | A299 Grade A | A299 Grade B | ||
ASTM A302/A302M | A302 Grade A | A302 Grade B | A302 Grade C | A302 Grade D |
ASTM A387/A387M | A387 Grade 5 | A387 Grade 9 | A387 Grade 11 | A387 Grade 12 |
A387 Grade 22 | A387 Grade 91 | |||
ASTM A515/A515M | A515 Grade 60 | A515 Grade 65 | A515 Grade 70 | |
ASTM A516/A516M | A516 Grade 55 | A516 Grade 60 | A516 Grade 65 | A516 Grade 70 |
ASTM A517/A517M | A517 Grade A | A517 Grade B | A517 Grade E | A517 Grade F |
A517 Grade H | A517 Grade P | A517 Grade Q | A517 Grade S | |
ASTM A533/A533M | A533 Grade A | A533 Grade B | A533 Grade C | A533 Grade D |
ASTM A537A537M | A537 Class 1 | A537 Class 2 | A537 Class 3 | |
ASTM A612/A612M | ASTM A612M | |||
ASTM A662/A662M | A662 Grade A | A662 Grade B | A662 Grade C | |
ASTM A841/A841M | A841 Grade A | A841 Grade B | A841 Grade C | A841 Grade D |
A841 Grade E | A841 Grade F | |||
EN10028-2 | P235GH | P265GH | P295GH | P355GH |
16Mo3 | ||||
EN10028-3 | P275NH | P275NL1 | P275NL2 | P355N |
P355NH | P355NL1 | P355NL2 | P460NH | |
P460NL1 | P460NL2 | |||
EN10028-5 | P355M | P355ML1 | P355ML2 | P420M |
P420ML1 | P420ML2 | P460M | P460ML1 | |
P460ML2 | ||||
EN10028-6 | P355Q | P355QH | P355QL1 | P355QL2 |
P460Q | P460QH | P460QL1 | P460QL2 | |
P500Q | P500QH | P500QL1 | P500QL2 | |
P690Q | P690QH | P690QL1 | P690QL2 | |
JIS G3115 | SPV235 | SPV315 | SPV355 | SPV410 |
SPV450 | SPV490 | |||
JIS G3103 | SB410 | SB450 | SB480 | SB450M |
SB480M | ||||
GB713 | Q245R | Q345R | Q370R | 18MnMoNbR |
15CrMoR | 14Cr1MoR | 13MnNiMoR | 12Cr2Mo1R | |
12Cr1MoVR | ||||
GB3531 | 16MnDR | 15MnNiDR | 09MnNiDR | |
DIN 17155 | HI | HII | 17Mn4 | 19Mn6 |
15Mo3 | 13CrMo44 | 10CrMo910 |
Product Display:
Manufacturing Technique
Cutting large steel plates as your requirements to make the surface of the plate bright by miling and grinding, also can make holes and make angle degrees,and can weld by your drawing.
For the thickness under 30mm, cutting by laser; For thickness over 30mm, mainly OXY-cut, flame cutting.
For the thickness 200mm steel plate, because during the flame cutting, the temperature is very high, so the cutting parts steel plate might be broken at the angle part, then our workers will repair the angles to be good condition.